A. WELBLUND ETAL 2,284,703 7 METHOD FOR CONTINUOUSLY MOLDING METALS June 2, 1942.

Original Filed June 1, 1938 9 SheefcsSheet l BY 6 Q ATTORNEY.

A. WELBLUND' ET L 2,284,703 ETHOD FOR CONTINUOUSLY MOLDING METALS June 2; -1'942 Original Filed June 1, 1 938 9 Sheets-Shaker. 2

ATTORNEY June 1942' A. WELBLUND ET AL 2,284,703

METHOD FOR CONTINUOUSLY MOLDING METALS Original Filed June 1, 1938 9 Sheets-Sheet s 'Junej: 2', 1942- A. WELBLUND ET AL 2,234,703

I METHOD FOR CONTINUQUSLY MOLDING METALS- Qriginal Fi led June 1, 1938 9 Sheets-Sheet 4 ATTORNEY ,J n 1942- A. VYVELBLUND ETAL I 2,284,703.

METHOD FOR CONTINUOUSLY MOLDING METALS Original Filed June 1, 195a 9 Sheets-Sheets 1 a? V /0/ a/ /03 I /0/ 11 8.9

:r I ,I' 10/ 88 84 80 .m Fre' Bayard I I ATTORNEY.

' June2,1942.

A.'WELBLUND AL METHOD FOR CONTINUOUSLY- MOLDING METALS Original Filed June 1, 1938 9 Sheets-Sheet 6 .7 v //4 g e zar'cii ATTORN EY June 2, 1942. A. wEpBLuND EI'AL 2,284,

' METHOD FOR: GONTINUOUSLY MOLDING METALS Qriginal Filed June 1, 1938 9 sheets-sheet '7 ATTORNEY.

June 2*, 1942. A. WELBLUND ETAL I METHOD FOR CONTINUOUSLY- MOLDING METALS 9 Sheets-Sheet a Original Filed June 1, 1958 INVENTORS .f/Zer/ Wr/ Zzl/zd ATTORNEY.

June 4 A. WELBLUND ET AL 3 7 METHOD FQRVCONTINUOUSLY MOLDING METALS Original Filed June 1, 1958 9 Sheets-Sheet 9 J2 H so 28 45 5.5 47

G I ATTORNEY.

Patented June 2, 1942 I METHOD FOR CONTINUOUSLi MOLDING METALS Albert Welblun'd and Fred amid, Sudbury, Ontario, Canada, assignors to The- Interna-. tional Nickel Companyof Canada, Limited.

Copper Cliff, Canada Ontario, Canada, a. company oi Original application June 1, 1938, Serial Nb.

211,116.- Divided and this application Decemher 3, 1940; Serial No. 368,294. In

continuously molding metal and, more particularly, to a method of making'a sound continuous elongated shape or casting of copper, especially superior in properties to a standard horizontal or vertical casting of customary electrolytic copperof standard quality produced in a conventional copper refinery.

Heretofore many attempts have been made to cast metals and alloys in the form of a continuous castingv or shape rather than as individual castings or shapes. The theoretical advantages of casting metal in theform of a continuous cast.- ing or shape over the almost universal commercial practice of casting in individual; casting or shape molds are many, including savings in capital invested in plants and equipment, economies in operation, elimination orminimizing of rejected metal andscrap metal such as croppings, sink heads, scalpings, etc., and the production of a more uniform product. Despite earnest endeavors of many workers in the art to design apparatus and to discover, methods for utilizing these advantages, the solution ofthis outstanding problem remained unaccomplished, at least so far as satisfactory commercial operation on an industrial scale was concerned. One of the principal operational difficulties was the sticking or adherence of the solidified metal to the wall of the mold. When the extent of the sticking effectively prevented by using a longitudinally divided mold whose sections are given a relatively slight but rapid vibration transversely to Canada May ll Claims. (Cl. 22200.1) The present invention relates to a method of We have discovered that sticking or adherence of the solidifying skin of a continuously molded casting or shape to the 'wall of the mold may be the direction of motion of the casting or shape and that this variation in the cross-section of the mold, contrary to expectations, does not have a deleterious but rather a beneficial effect on the surface appearance and physical properties 0 the molded metal.

It is an object of the invention to provide a method of making a continuous ingot, casting or shape which is substantially free from flaws, pipes, etc. and which is characterized by'longitudinal uniformity in density, oxygen content,

electrical conductivity, physical properties, etc; and preferably by substantial symmetry of metallographic structure incross-section.

The invention has for a further object the production of elongated copper or other metal 01' alloy castings or shapes having a metallographic structure comprising a relatively small central core of columnar crystals arranged substantially parallel to the longitudinal axis of the casting or shape, a relatively large sunburst of col-.

umnar crystals surrounding the central core and arranged substantially.perpendicular to the walls was so great that the withdrawing mechanism could no longer pull the casting or, shape out without damaging the surface of the casting or shape, abreak or rupture in the continuity of the process resulted and it was often necessary to destroy themold in order to free the casting or shape. On the other hand, when the withdrawing mechanism continued to pull the casting or shape out, the solidified skin would rupture. A rupture outside the mold permitted the still molten metal to gush 'forth in uncontrollable streams causing damage to. equipment and inof the mold, a relatively narrow band of small crystals or grains adjacent to the outer periphery of the casting orv shape,'and an external surface skin coating ,the exposed portions of the casting or shape.

It is another object of the invention to provide a method of producing continuous, elongated jury or even death to the operators; While not so disastrous, ruptures within the mold permitted the metal in the still molten core to flow to the vmold wall through the rupture, forming an unsatisfactoryand commercially unacceptable product. The process, moreover, could not continue satisfactorily after pieces of the skin had frozen fastto the mold wall.

hollow or tubular castings orshapes which are substantially free from flaws, defects, etc. and

.that possess longitudinaluniformityin density,

oxygen content, physical properties, etc. and

preferably substantial symmetry of metallo-- graphic structure in cross-section.-

Moreover, the invention provides a method of making a sound continuous ingot, casting or shape ina sectional mold, the sections of which vibrate substantially transversely to the longitudinal axis of the ingot, casting or shape, said method being capable, of producing continuous ingots, castings and shapes at'satisfactory speeds for commercial production on an industrial scale.

Other objects and advantages of the invention will become apparent from the following descripcomposite side elevational view, partly'in section or an apparatus adapted to carry out the present invention;

Fig. 2 is a side elevatlonal view of the upper part of the apparatus illustrated in Fig. 1 drawn on an enlarged scale with certain parts omitted or broken away for the sake of clarity and with certain portions in section along the line 2-2 of Fig. 3;-

Fig. 3 depicts a top plan view of the apparatus shown in Fig. 2;

Fig. 4 shows an enlarged sectional view of the means for vibrating the mold taken substantially along the line 4-4 of Fig. 3;

Figs. 5 and 6 are sectional views on the line 5-5 of Fig. 4, with certain parts omitted for the sake of clarity, showing the arrangement of eccentric parts in two different positions of adjustment for varying the extent of vibration of the mold sections;

Figs. 7 and 8 represent, respectively, top and side views of a two section mold for molding cylindrical ingots, castings and shapes;

Fig. 9 illustrates a top plan view of a four section mold for molding ingots, castings and shapes of quadrilateral cross-section; v

Fig. 10 is a side elevational view on an enlarged scale of the withdrawal device, looking toward the left in Fig. 2 with the gears removed for sake of clarity but their positions indicated in dotted outline;

Fig. 11 is a top plan view of the withdrawal device shown in Fig. 10, with certain parts omitted and broken away to more clearly disclose the means for varying the pressure on the rollers;

Fig. 12 shows a top plan view and Fig. 13 a side elevation view of a power saw and associated parts mounted on a movable carriage for severing the continuously molded ingot, casting or shape into convenient lengths, certain parts being broken away to reveal normally concealed parts;

Fig. 14 illustrates a. top plan view, with certain parts broken away to reveal structure on a lower plane of a modified form of cooling device into which the ingot or casting is conducted upon leaving the dynamic mold;

Fig. 15 is a vertical sectional view of the cooling device illustrated in Fig. 14, the portion above the line AB-AB being taken along line B-B and the portion below line ABAB being taken along line AA of Fig. 14;

Fig. 16 represents a photomacrograph of a cross section and Fig. 17 that of a longitudinal section of a copper ingot molded by the process embodying the present invention;

Fig. 18 depicts the structure of the casting in horizontal section near an edge, at a magnification of about 200 diameters;

Figs. 19 and 20 show the structure of the casting in horizontal section about 0.08 inch and about 0.5 inch from the surface skin, respectively, at magnifications of about 100 diameters;

Fig. 21 is a representation of the grain or crystal structure in cross-section at the center of the casting at a magnification of about 750 diameters;

Fig. 22 depicts a top plan view of a modification of the apparatus adapted for molding hollow or tubular ingots, castings or shapes, certain parts being omitted; and

- alloys.

Fig. 23 is a verticalsectional view. along the line 23-23 of Fig. 22. 1

Generally speaking, the method of the present invention contemplates the production of elongated ingots, castings and shapes of metals and As carried into practice the invention comprises introducing molten metal into a confining space where heat is abstracted to cause the metal to solidify into an ingot, casting or shape having a cross-sectional contour substantially conforming to that of the confining space and, during the period of solidification, alternately increasing and decreasing the cross section of said space to prevent adherence of the solidifying metal to th walls defining said space. For molding ingots. castings and shapes of longer axial length than the confining space, the molten metal is preferably introduced continuously at at rate correlated with the rate of solidification and withdrawal-of the solidified metal from the confining space. 'Where the axis of the confiing spac ismore or lessvertical, it is necessary to support the ingot, casting or shape as it is being withdrawn to prevent the whole body of metal from falling out of the confining space. By regulating the supporting and withdrawing forces acting on the solidified metal it is easy to control the rate of withdrawal from the confining space and to correlate it with the rate of solidification of the molten metal. Continuity of operation can be maintained by severing selected lengths from the end of the moving ingot, casting or shape.

A suitable apparatus for carrying out the process of the present invention is disclosed in and forms the subject matter of the claims of our prior copending application, Serial No. 211,116, filed June 1, 1938, of which the present application is a division. The apparatus includes a dynamic mold constituted of a plurality of mating sections which are vibrated in coordination with each other. The vibrations may be imparted to the sections in any appropriate manner, such as mechanically, electrically, pneumatically, or the like. The mating sections of the mold define an open ended chamber, the cross section of which constitutes the shape on a transverseplane of the ingot casting or the like, which is to be made. One end of the mold is open to permit the continuous introduction of molten metal therein and the other end of the mold is likewise open to enable the continuous ingot, casting or shape to be withdrawn continuously. The bottom of the mold is initially closed with a starting plug or dummy bar. As the continuous casting is produced, the starting plug or dummy bar is continuously moved away from the withdrawal end of the dynamic mold. This movement may be accomplished in any suitable manner, such as by advancing or pinch rollers driven by suitable mechanism, by jack screw which is associated with appropriate means, etc.

In operating the apparatus molten copper or another metal or alloy may be poured continuously into the mold while the sections are vibrated. These sections mate with each other so closely that there is substantially no clearance between them in the closed position although they preferably do not actually touch. By subjecting 'the sections to coordinated vibration of small conductivity such as copper or its alloys and are cooled, preferably by passing water or other cooling fluid upwardly through a tortuous path in a cooling Jacket or channel formed in the interior of each section. By the time the metal arrives at the bottom of the mold, it is solidified in the form of a dense ingot, casting or shape.

To set the apparatus into operation, a sumcient amount of solidified metal is allowed to accumulate within the mold above a starting plug or dummy bar which isthen moved at a speed coordinated with the rate of solidification of the metal within the mold and the rate at P which the molten metal is poured into the mold.

In other words, the solidified ingot, casting or shape is moved from the mold as it is formed. The continuous ingot, casting or shape thus producedhas high density throughout its cross section and every region is autogeneously bonded to or integrally united with an adjacent region.

' Furthermore, the skin on the outer surface of .venient to construct the divisions or units in superimposed vertical relationship to each other. The upper division or unit, indicated generally by reference character A, comprises the apparatus for pouring, molding and solidifying the metal. Thereunder is located the intermediate division or unit designated generally by the ref; erence character B which includes means for withdrawing the ingot, casting or shape from division or unit A at a properly correlated speed and feeding it into the lower division or unit, marked C as a whole, where a device'is mounted for severing the ingot. casting or shape into desired lengths as it is moving. For convenience, the apparatus will be described in greater detail under these three divisions or units.

Division or unit A includes a furnace or ladle i tiltably mounted upon brackets 2 which are secured to uprights or structural columns 3. A main beam 4 supports and holds the uprights 3 in proper position. The furnace I may be of any suitable type for preparing and/or holding a considerable quantity of metal to be molded at the proper temperature and under proper conditions for pouring, as will be. well understood by those skilled in the art. It is preferred to use an electric furnace such as an arc furnace or an induction furnace. A pouring lip or spout 5 is provided on furnace l adapted to direct a stream of molten metal from the furnace when it is tilted by raising cable 6, or by any other appropriate tilting means. Below lip 5 is a pouring vessel 1 having a pool 8, into which the stream of metal from the spout 5 falls, and having an outlet 9. Supporting the pouring vessel 1 is a pouring platform III mounted upon a post I I which forms part of framework I2 of the upper division or unit A. The quantity of molten metal flowing from outlet 8 per unit of time may be controlled by varying the height of the molten metal in pool 8, which in turn depends upon the rate of flow of metal from the furnace l. The

pouring vessel I is not indispensable but it facilitates controlling the direction and rate of flow of molten metal at the proper temperature into the mold could be used in place of the aforesaid apparatus as is obvious to those skilled in the art. Thus, an under pour or enclosed ladle with a skimming bridge may be used to insure pure metal free etc. I

Reference character I3 is the generaldesignation of an open ended dynamic mold into which the stream of molten metal from outlet 9 from slag, oxides, contamination, etc.,

of the pouring vessel 1 is directed through the,

upper end and from the lower end of which a continuous molded ingot, casting or shape of solidified metal is withdrawn. The dynamic mold I3 is constituted of a plurality of mating sections I4. (See Figs. 7, 8 and 9.) The number of sections may vary depending upon the size and configuration of the ingot, casting, shape or the like which is to be produced. Satisfactory results have been obtained with molds having two sections such as illustrated in Figs. 7 and 8 and four sections as shown in Fig. 9. As stated 'hereinbefore, the mold sections may be made of any suitable metal or alloy. Silver and silver alloys, copper and copper alloys, etc., which have relatively high thermal conductivity may be used to advantage. Clad and plated or coated metals may also be successfully employed for the mold sections, for example, a copper-cadmium alloy mold with a facing of electrodeposited chromium gave good results in practice. The facing or coating metal or alloy may be applied by electrodeposition, spraying, etc., as those skilled in the art will understand.

The apparatus illustrated for vibrating the mold sections is adapted for use with a two section mold, as may be clearly seen in Fig. 3, but

the stream of metal into a mold to be described hereinafter. Any other suitable arrangement of furnaces, ladles, etc. which would enable an opit is evident that it may be modified without invention to accommodate molds of any desired number of sections. The shape of the ingot desired will determine the shape of the mold cavity which may be quadrilateral as inFig. 3, circular as in Fig. 7 or any other desired shape. Each mold section is provided with a cooling channel [5, an inlet Hi to admit cooling water or other fluid from any suitable source and an outlet through which the warm or heated cooling water is discharged (see Figs. 3, 7, 8 and 9) Machine screws l9 secure each mold section to a yoke l8 which is adapted to reciprocate or move back and forth upon supporting guide rods 20 whose ends pass through and are supported by openings in pedestals 2i forming part of the framework 12, as may be clearly seen in Figs. 2 and 3. The rods 20 are conveniently made in the form of long bolts having heads 22 at one end abutting against the adjacent pedestals with nuts 23 and lock nuts 24 at the other end likewise abutting against the adjacent pedestals and holding the parts in assembled relation. The ends of the yokes l8 have cylindrical bores provided with bearing surfaces accurately fitting around rods 20 so as to minimize undesirable vibration. In order to provide space for reciprocation of the mold sections, each end of the yokes I8 is somewhat narrower, than half the length of bar 20 extending between the pedestals 2| (see Fig. 3). Preferably, the yokes do not touch each other in the position of minimum clearance and the contacting surfaces of the mold sections are advantageously rabbeted as at orator to direct 8- resu ab e continuous stream 01 tacting surfaces of the mold sections are shown as longitudinal splits or Joints between adjacent sections. This split or Joint may be parallel to the vertical axis of the mold, or may be inclined at any angle, or may be of any appropriate shape, provided the sections are mated. The yokes and associated parts rigidly support the mold sections l4 in an upright position at all stages of the reciprocating movement.

Rotating eccentrics, indicated generally by reference numeral 21 are mounted in housings 23 on framework l2 and are adapted to impart the desired reciprocatory motion to the yokes l3 through connecting rods 29 (see i 4). Each connecting rod is articulated to the corresponding yoke by means of a cross-head 30 and a wrist pin 3! as clearly shown in Figs. 1, 2 and particularly 4. The ends of the connecting rod 29 are advantageously provided with right and left hand threads, which are screwed into suitably drilled and tapped holes in cross-head 30 and an eccentric head 32, respectively. Locknuts 33 lock the connecting rod and associated parts in any desired position of adjustment.

, The eccentric head 32 may advantageously be an annular forging with a projection in which a tapped hole is provided to receive an end of the connecting rod 29 as shown in Figs. 2, 3 and 4. By providing the inner surface of the eccentric head with a rabbet; a shoulder is formed on which an outer race of a ball bearing 35 may rest and be firmly held by a ring clamp 36 and cap screws 31. A top cover plate 33 is appropriately secured to the ring clamp 36 to close the upper end as illustrated in Fig. 4. The contacting faces of housing 23 and eccentric head 32 are provided with loosely fitting tongues and grooves, the amount of play slightly exceeding the maximum throw of the eccentric 21. This structure, as clearly seen in Fig. 4, permits the free movement in any horizontal direction of the eccentric head 32, but at the same time prevents accidental displacement thereof from housing 23 during repairs, adjustments, etc.

The eccentrics 21 are secured to and driven by shafts 39 which extend into the'housings 23 from the bottom thereof; To close the lower end of the housing 23, a bottom cover 40 is fastened thereto by cap screws 4| while cap screws 42 secure housing 23 to the framework i2. As seen more clearly in Fig. 4, the bottom cover may comprise a main plate 40a, a felt or other fibrous packing ring 49b such as asbestos, rubberized asbestos and the like, and a retaining ring 400 appropriately held together by a plurality of machine screws 40d. The felt packing ring 40b tightly engages shaft 39 to prevent the escape of lubricating agents from the housing 23.

Each shaft 39 is provided with a collar 43 near its upper end. Against the lower side of collar 43, a lock nut 44 holds an inner race 45 of a ball bearing 46, the outer race 41 of which is secured in any appropriate manner to the inner wall of housing 28, while against the upper side of collar 43 the inner race 48 of ball bearing 35 is held by a flanged eccentric ring 49 and a disc 50. The end of shaft 39 which extends beyond collar 43 is I eccentric with respect to the axis of the shaft.

The inner and outer walls of eccentric ring 49, which fits down over the end 5|, are eccentric with respect to each other. This is clearly illustrated in Figs. 5 and 6 where the degree of eccentricity has been exaggerated in order to illustrate the principle of this phase of the invention. These views are taken on the line 5-5 of Fig. 4 with the inner race 43 of ball bearing 35 removed for sake of clarity. The outer circle therefore represents the periphery of collar 43 which is concentric with the shaft 39, this common center being indicated by the reference character 390. The inner circle represents the periphery of the eccentric end 5i which has its center oil-set from center 390 of shaft 39 as shown at 5lc which also represents the center of the inner wall of the eccentric ring 49. The center of the outer periphery of eccentric ring 49 is off-set as shown at "490. By rotating the eccentric ring 49 with respect to the shaft 39, the amplitude of the reciprocatory motion imparted to the cross heads 30 may be varied, as clearly illustrated in these figures. In Fig. 5 the position of maximum throw is shown, i. e., center 490 of eccentric ring 49 is as far from center 390 of shaft 39 as possible, while in Fig. 6 an intermediate position is depicted. It is evident that by making the distance from 39c to 5ic the same as the distance from Sir: to 49c, it is possible to obtain any desired degree of eccentricity from zero to twice this said distance by rotating the eccentric ring 49 through 180 with respect to the shaft 39. A convenient means for locking eccentric ring 49 in any desired position of adjustment comprises a set screw 52 adapted to be inserted through disc 56 into any one of a plurality of holes provided in the top of ring 49 Since disc 59 is fixed to the end 5i of shaft 39 by two or more cap screws 59a, it will be seen that eccentric ring 49 is thereby securely held in the desired position relative to the shaft 39 (see r Fig. 4).

Rotation may be imparted to shaft 39 by any appropriate means, such as an electric motor 53, through a flexible coupling 54, shafts 55 and bevel gears 56 and 51 keyed or otherwise fixedly secured to shafts 39 and 55, respectively (see Figs. 3 and 4) Gear boxes 58 are affixed to framework I2 to house the gears 56 and 51 and to provide mountings for bearings 59 in which shafts 39 and 55 are journaled. To assure quieter and more efiicient operation, the gear boxes 58 are preferably filled with some suitable gear lubricant which is prevented from'escaping by oil seals 60.

Fig. 3 shows a convenient arrangement of the parts for vibrating the mold which has proved satisfactory with a two section mold. In certain instances when it is desired to use a four section mold of the type shown in Fig. 9, the arrangement of Fig. 3 is modified, for example, by including a further rotating eccentric 21 and associated Parts at each of the two other sides of the framework i2 and by arranging the shafts 55 approximately parallel to the sides of framework i2 to drive the four shafts 39, as will be apparent to those skilled in the art.

The molded ingot, casting or shape still retains considerable heat as it leaves the dynamic mold. In order to abstract the excess heat before the ingot enters the withdrawing means in division or unit B, a cooling device indicated generally by reference numeral 6i is provided beneath the dynamic mold. Conveniently, cooling device 6i may comprise an open ended container 62 having a dam 63 at the lower end made of rubber, rubberized asbestos, or other suitable yielding material, a water supply conduit 64 opening into the container 62 adjacent the dam 63, an overflow basin or trough 65 surrounding the upper end of the container 62 and a drain pipe 66 leading from the bottom of the overflow basin, as seen in Figs. 1 and 2. The dam 63 is provided with an opening corresponding in shape to the cross section of the ingot, casting or shape to prevent escape of the ass-mos cooling fluid while parmittingithe'ingot, casting or shape to pass therethrough. Supporting member device 8i and to secureit to framework:

Division or unit B includes a framework 88.

preferably of cast iron or steel, having suitable uprights and cross members to "form a sturdy, rigid support for division or unitAas well as a mounting for a withdrawing or feed device indiormeans 81 is'lprovid'ed to positionlthe cooling 1 sleeve 82 in spacing the toggle arms 18 of frame 8| when the nuts 88 i are tightened on the threaded ends of shaft 8| and additionalfunctionsas well, as will be clear from the'following description. Itwill be seen" from Figs. 10 and 11 that the shaft 8| is slidable in slots 81 I in the links 88 and that a leafspring 88, mountcate'd generally by reference numeral 88 and'a guide designated as a whole by reference numeral I8. Cross members of framework 68 may form a platform II on'which both the feed device 68 and guide I8 are mounted.

' in Figs. 1 and 2 so that front and side views may be seen, although this arrangement need not be followed in practice. Fig. 10 shows the withdrawal device 68 on a larger scale looking toward the left of'Figs. 1 and 2 with the gears removed for the sake of clarity. Corresponding parts in the two mechanisms have been given the same reference numerals.

A support I2 comprises a base 13, two uprights I4 secured'at one end to the base 13 and two cross bars 15 joining the other ends of uprights I4 and forming therewith an opening through which the ingot may pass, as seen in Fig. 11. The base 18 is rigidly fastened to platform 'II and each has an opening ,to allow the ingot to pass. A stub shaft I6 is mounted at each side of each upright 14 adjacent the base 13 by means of clamps 11, the four stub shafts extending inwardly and being aligned in pairs at the corresponding sides of uprights I4. On each stub shaft is journaled one end'of it toggle arm l8. Spacers I8 connect the two arms 18 that are journaled to the paired or aligned stub shafts, thus forming two swinging frames 88 and 8|, one on either side of the ingot. Trunnions 82 of rollers 83 are journaled on each of the swinging frames 88 and BI adjacent the swinging end by hearing caps 84. The trunnions 82 are shown extending beyond the toggle arm 18 and on each extension is rotatably mounted one end of a further toggle arm 85 whose other end is pivotally secured to a cross-head 86 slidably mounted, one at each side, to dove-tail guides 87 on the uprights 14. The toggle arms may conveniently be held on the trunnions 82 by means of retaining discs 85a and cap screws 851) as shown in Figs. 2'and 11. The rollers 83 are thus held in parallel relation regardless of the distance between them. In order to keep the rollers in close contact with the ingot, means are provided to force the swinging frames 88 and BI toward the ingot comprising two connecting links 88 having a pivotal connection at oneend to a shaft 88 passing through extensions 88 on the toggle arms 18 of swinging frame 88 and having a slidable and pivotal connection at an intermediate point with a similar shaft 8I passing through extensions 88 on the toggle arms 18 of swinging frame 8|. A sleeve 82 surrounding shaft 88 assists in holding the arms I8 of frame 88 properly spaced when the nuts 83 at the ends of shaft 88 are tightened. Surrounding shaft 8i is a sleeve 84 havingan inwardly threaded hollow extension 85 integral therewith (see Fig. 11). Sleeve 84 serves the same function as edin shackles 88 at the'en'ds of the links 88 opposite the ends conne'ctedtoshaft 88. tends to force theshaft 8i to the right through the medium of an adjusting screw I88 threaded at one end into the hollow extension 88 and rotatably mounted at the other end in a head I8I against which spring 88 bears. The connection between the shackles 88, the spring 88 and the links 88 may be made by bending the ends of the spring 88 and the ends of links 88 around shackle pins 88a. The head IN is preferably loosely connected with the center of spring 88 by a bar lflla'and cap screws I8Ib, as depicted in Figs. 10 and 11. Cross-bar I82 is welded or otherwise secured to the ends of links 88 adjacent theshackles to position and slidably hold the head I8I. By rotating the screw I88, it is possible to adjust the pressure of the rollers 83 on the moving ingot to any desired extent and if a single leaf spring is not powerful enough it is evident that additional leaves may be used. Hand wheel I83 makes the rotation of adjusting screw I88 simple and easy for the operator.

At least one of the rollers 83 in the withdrawal device 88 is positively driven at a controllable speed, for example, by a variable speed electric motor I84 set on a bracket I85 mounted by any appropriate means on framework 88 (see Figs. 1 and 2). A gear I88 is keyed to the trunnion 82 at the adjacent end of the driven roller 83 and meshes with a pinion I81 keyed on a shaft I88. Bearings for shaft I88 are provided in the adjacent upright I4 and an auxiliary upright I88 also mounted on base 'I3.- If necessary a third bearing (not shown) could be provided on framework 68. A gear H8 meshes with a pinion III on the motor shaft H2 and transmits the rotary motion of the motor shaft to shaft I88 on which gear H8 is keyed, thereby setting pinion I81, gear I88 and roller 83 in rotation. As rollers 83 are forced by spring 88 firmly into contact with the ingot, a positive withdrawing force is exerted which assures the safe and controlled withdrawal of the ingot at freezing metal is supported in a positive manner during the molding operation. Accordingly, ruptures in the surface and body of the ingot are prevented and separation of the solid ingot from the metal undergoing freezing isprevented. In contrast tothe foregoing it was necessary in prior art continuous casting apparatus for the ingot to be forcefully pulled or jerked from the mold, and whenever the freezing metal had adhered to the mold wall a rupture in the skin or body of the ingot would be produced. This diiiiculty in prior art processes has been entirely overcome in the present invention because sticking of thefreezing metal to the mold ,walls is positively prevented by the transverse vibrations of the mold sections and the withdrawal device not only safely withdraws the ingot from the mold at a controlled rate coordinated with the speed of pouringand cooling but also supports the ingot and superimposed molten and freezing metal in a positive manner.

Satisfactory results have been obtained in practice when both rollers 63 of the withdrawal device 69 were power driven, and in Fig. 10 the necessary gears for accomplishing this result have been indicated in dotted lines. It is evident from this view that each roller 83 has a gear I06 keyed to the trunnion 62 and that each meshes with a pinion I01 suitably mounted on shafts I and Illa extending between the upright I4 and the auxiliary upright I09 so thatthey also mesh. The direction of rotation of each of these gears is indicated by the arrows in Fig. 10. If desired, shafts I66 and I08a may be made integral with the two stub shafts I6 at that side of the withdrawal device 69 and be rotatably mounted by bearing caps 11 in the same manner as hereinabove described in connection with the stub shafts I6.

Division or unit C comprises a framework II3, the lower end of which may be set in a suitable foundation (not shown). It is made sufficiently strong to give rigid and firm support to divisions or units A and B as well as to provide the mounting for a cut-off mechanism. The cut-off mechanism includes a carriage II4 having tongues III slldable in'vertical grooves formed in the framework II3. A power saw H6 is mounted for horizontal movement on and vertical movement with the carriage H4. The power saw II6 comprises a frame III mounted for horizontal reciprocation on guides II3 on the carriage II 4. On one of the vertical sides of frame II! which lies parallel to the direction of motion along guides I I8 an electric motor H9 is slidably mounted in vertical guides I20 and is capable of being locked in any desired position of adjustment along these guides by lock nuts I 2I. A pulley I22, keyed to the shaft of motor H9, is provided with a plurality of V-shaped grooves in its periphery. A similar pulley I23 is fixed to a shaft I24 suitably journaled in the frame I". Endless v belts I25 pass around the pulleys I22 and I23 and transmit the torque of the motor II! to shaft I24. In order to reduce the speed of rotation, a worm I26 is keyed to shaft I24 to drive a relatively large gear I21 on a vertical shaft I26 suitably journaled in the frame A second vertical shaft I29 journaled in frame I" carries a saw blade I30 at the upper end and a gear I3I which meshes with a similar gear I32 on the shaft I26. It will be observed from Fig. 13 that shaft I29 is near the right extremity of the frame II! and that the saw blade I30 extends there beyond a distance somewhat greater than the largest dimension of the cross section of the ingot to be severed. It is for this reason that two vertical shafts have been used, because if gear I21 were on shaft I29 it would interfere-with the operation of the saw. This diflficulty is avoided by journaling the shaft I26 at the left of shaft I29 and by making the latter short enough that gear I21 can be placed below its lower end, as seen in Fig. 13. n

The frame II! of the power saw H6 is moved horizontally along the guides II3 on carriage II4 by means of a screw I33 rotatably mounted in a pedestal I34 at the right'end of carriage I I4 and which engages a nut I35 on the frame III. Rotation is imparted to' the screw I33 by a hand wheel I36 on a shaft I31 which also carries a worm I36 that meshes with a gear I39 on the screw I33. It will be clear to those skilled in the art that screw I33 could be mechanically driven, if desired. The pedestal I34 carries a pair of laterally extending arms I40 at its upper end on which a shaft I is journaled. Shaft MI is provided with a hand wheel I42 at one end which extends beyond the arm I40, a set of right hand threads I43 and a set of left hand threads I44. Clamp arms I45 are pivoted at one end to pedestal I34 by pins I46 and lugs I41 and carry nuts I48 and I49 at the other end which engage threads I43 and I44 respectively. Rotation of shaft I by hand wheel I42 will therefore cause the free ends of clamp arms I45 to move toward or away from each other. The opposed faces of the clamp arms I45 are provided with removable jaws I50 which are adapted to engage the ingot as it moves downwardly when hand wheel I42 is rotated in the proper direction. One set of jaws I60 may be shaped to clamp a circular ingot, casting or shape, another set to clamp a rectangular ingot, etc., and the proper set mounted in the clamp arms I45 to correspond to the shape of the ingot to be cast.

The carriage H4 is balanced by counterweights I5I connected to some convenient part of the carriage by ropes I52 passing over sheaves I63 suitably journaled in the framework II3 ofdivision or unit C. When it is desired to .cut off a length of the ingot, casting or shape, the operator turns hand wheel I42 to clamp jaws I50 tightly against the ingot, switches on the power to motor H3 and then turns hand wheel I36 to force the now rotating saw blade I30 through the ingot. It is evident that the carriage is moved downwardly at the same speed as the ingot so that the blade I30 may operate without binding and without interfering at all with the continuous molding carried out in the dynamic mold. As soon as the ingot is severed, hand wheel I36 is rotated in the opposite direction to return frame II! to the original position whereupon the hand wheel I42 is rotated to release the jaws I50 and permit the carriage to be returned to its upper position. I

A modified form of cooling device, illustrated in Figs. 14 and 15, has been advantageous under certain circumstances. A container designated generally by reference numeral I54 is adapted to be secured to framework I2 in the same relative position as container 62 shown in Figs. 1' and 2. n

The container I54 comprises an upper cylindrical casing I55 and a lower cylindrical casing I56 provided with a bottom wall I51 having an aperture I58 through which the ingot is adapted to pass. A yielding dam I59 having an opening preferably slightly smaller than the crosssection of the ingot or casing is secured to the bottom wall by a retaining ring I60 and machine screws I6I. The dam I59 may be made of rubber,. rubberized asbestos, felt, or similar material which will tightly embrace the ingot, casting or shape and thereby prevent excessive leaking of cooling fluid around theingot as it moves out of the cooling container. An inlet connector I62 is provided near the bottom of the container I 54 to which an inlet pipe communicating with any suitable source of supply may be connected, the cooling fluid flowing up The upper and lower casings I55 and I56 are preferably flanged at their meeting ends to pro vide a fluid tight joint when bolted together by bolts I65 with an interposed gasket I66 of rubripheries so as to receive and-guide the longitudinal edges of the ingot, castingor shape as clearly shown in Fig. 14. Ithas been found, advantageous in practice to make each of the rollers I69 of five. freely rotatable discs, as may be seen in Fig. .14. In this way the difference in peripheral speed of the rollers at various marred. The rollers I of the lower set of guide rollers I68 may have cylindrical surfaces to points along the grooveis largely eliminated and the surface of the ingot, casting or shape is not bearagainst the sides of the ingot. For con- 1 venience of illustration in elevation. Fig. 15 depicts thepairs of opposed rollers of the upper and lower sets in the sameplane whereas .the

- planes of thepairs' of rollers-there shown are actually offset 45, as may be seen in Fig. 14.

ThepartohFig. 15 above line AIS-AB is taken along the line B-B of Fig.1 4 and thepart. below line AB-AB istakerr along line A A of A convenient means for rotatably securing the rollers I69 and I16 to the walls of the container comprises segmental blocks I1I fastened to the walls of the container by machine screws I12, U-shapcdframes I13 pivotally mounted at each splashing, a baffle plate IBI in the form of an annulus of sheet metal may be placed at the top of t the overflow basin I63. A convenient means for holding the baffle plate I8I in position comprises bolts I62 welded to the periphery of the plate which seat in slots in the upper edge of the overflow basin I63, as seen in Fig. 14. Nuts I63 hold the baflle plate I6I in position.

A flange I64 is welded or otherwise secured to the container I54 to support the cooling device on the framework. of division or unit A.

The apparatus is put into operation by filling the cooling channels I5 of the mold I3 with water, moving the mold sections I4 to the position of minimum clearance, placing the head of a dummy bar or'starting plugat about one-third of the height of the mold up from the bottom, and then pouring molten metal intothe'chamher thus formed from furnace I and pouring vessel 1, as may be clearly seen from Fig. 1. After sufficient time has elapsed for the metal first poured to have solidified around a bolt, hook, or other device attached to the top of the dummy bar, the mold sections I4 are vibrated and the withdrawal mechanism 69 started. It has been found that satisfactory results are ob tained by vibrating the mold sections from about free end to one ofthe segmental blocks III by I machine screws I14, and shafts I15 journaled in the arms of the frames I13 on which the rollers I69 and I10 rotate, as may be seenin Figs. 14 and 15. An aperturedlug I16'is welded or otherwise secured to the cross member of each frame I13. Journaled in each apertured lug I16 is an adjusting screw I11 having a head I18 bearing against one side of the lug and a collar I19 bearing against the other side. The other end of each screw I11 is threaded through a tapped opening in the wall of the container I54 reinforced by a nut I86 welded thereto, whereby rotation of the screw I11 swings the rollerjourmailed in the respective frame I13 toward or away from the ingot or casting. Lock nuts I not shown) may be used either inside or outside the container wall to lock the rollers in the proper position to guide the ingot or casting.

It has been found convenient in practice to square the ends of the screws I11 to receive a wrench for turning the same. It will be apparout to those skilled in the art that the rollers I69 and I10 may be readily replaced by similar I rollers having peripheral grooves contoured to fit any desired ingot, casting or shape; e. an.

if the ingotwere circular in cross-section the grooves in the peripheries of the rollers would have substantially the same radius of curvatrue. as the ingotL-This arrangement'of guide rollers in close proximity to the dynamic mold provides lateral support tothe ingot. casting or sha e at the time when it is mostneeded.

It has been found in practice that currents of hot water rising in the container I54 around the ingot,.casting or shape sometimes splash out of the container against the bottom of the mold. In order to prevent such undesirable ing and at the same time is supported in a posi- 100 to about 1500 times per minute and having them move a very small distance, say, about two thousandths to about fifty thousandths of an inch. It is not essential to the production of ingots, casting or shapes free from fins, projections or the like that the mold sections actually touch in the position of minimum clearance. The rate at which the metal is withdrawn must be coordinated withthe rate at which it is poured. and both of these rates must be governed by the cooling capacity of the machine. In other words, the ingot is continuously withdrawn as it solidifies and becomes self sustaintivc manner. Satisfactory sound continuous ingots, castings and shapes of copperhave been produced at a rate within the range of about f twelve inches to about twenty-four inches per minute in a two-section mold of the type illus-' trated inFig 3 in which the molding cavity had a cross-sectional area of about four square inches. In molds having a cross-sectional area of about nine square inches satisfactory results have been obtained at rates within the range of about nine to about fourteen inches per. minute. It is to be understood that the aforementioned casting rates are illustrative only and are not to be construed as limiting the process either to the stated minimumfor maximum rate. Beneath the vibrating mold the coolingdevice 6| fluid may be arranged to dissipate excess heat of the metal which is not removed in the mold.

The dummy bar or starting plug is moved gradu-- ally downwardly until the ingot itself reaches the cut-oil? mechanism M3,. The dummy bar is then disconnected and set aside for re-use when the apparatus is again set into operation. The pouring ispreferably conducted continuously and a dense continuous casting in the form of, say, a cast copper bar is produced which may be cut into suitable commercial lengths for further operations such asrol-ling, drawing, piercing, etc.

. It is clear that in case a continuous bar, strip or sheet were desired, the cut-off mechanism II3 couldbe replaced by suitable means to work the ingot into the desired shape, as those skilled in l 15 the art will understand.

As a specific example of the process. of .the present invention, a 2350 pound charge of tough pitch copper, prepared in an electric furnace,

entered the cooling channels of the mold sections at a temperature of about 36 F. and flowed out at a temperature of about 48 F. The flow of water amounted to about 20 Imperial gallons per minute.

It has been found that the present process produces, for instance, a dense copper ingot, casting or shape superior in the symmetry of its metallographic structure in cross section and in its longitudinal uniformity of structure, composition and properties to copper prepared for casting in the same manner but which was cast in stationary vertical or horizontal molds. The surface appearance of the cast copper ingot of the present invention is satisfactory, being completely free from cracks, fissures, cold sets or shuts and other defects. The ingot, casting or shape is straight and uniform in size throughout its length and is free from "set ends which have to be cropped oil and from surfaces requiring scalping."

In cross-section the macrostructure of the ingot or casting is characterized by a narrow band of equiaxed. chill crystals extending from the edge to a depth of about a zone of sunburst crystals or radial crystal aggre gates growing in columnar form toward the cooling centerof the casting, and a central zone of relatively small extent comprising columns of crystals growing within the "sunburst or radial columns along the longitudinal axis of the ingbt or casting, as may be seen in Figs. 16 and 17. The radial columns grow substantially perpendicular to the adjacent side of the. casting. Regardless of the length of the ingot, casting or shape produced, its structure is substantially uniform throughout the whole length, the section depicted in Fig. 17 being typical of the macrostructure on a longitudinal section through the axis of the ingot. No cracks, fissures, pipes, shrinkage cavities, or like defects are present in the ingots, castings or shapes produced in the apparatus and by the process embodying the present invention.

When tough pitch copper is cast in the apparatus and by the process embodying the present invention, an ingot, casting or shape is produced having high average density combined with satisfactory and acceptable uniformity of density across the cross-section and throughout the length of the ingot, casting or shape. The cast bars of the present invention are characterized by having the highest density in a zone of considerable cross-sectional area along and surrounding the longitudinal axis of the bar. While somewhat lower in density than the central zone, the outer zones are free from objectionable porosity and have in general a higher density than corresponding outer zones of prior vertical cast bars. It is to be noted that the slightly lower density of the outer zones does not detrimentally affect the merchantability of the bars of the present invention and does not adversely afiect the working of the bar or the subsequent fabrication thereof into acceptable and satisfactory articles of manufacture. In contrast to the aforesaid, a bar of the same copper cast in conventional vertical molds exhibited lower density across the entire section with lowest density in a zone near the center or axis of the bars. The average density of the tough-pitch copper cast in accordance with the teachings of the present invention is about 8.83 as compared with about 8.73 when .cast in vertical and about 8.5 when cast in horizontal molds. In prior horizontal and vertical cast bars, moreover, the density varies with the distance from the bottom of the casting whereas the bars of the present invention have consistently uniform high density along the whole length.

Microscopic examination of the structure of tough-pitch copper castings produced by the method embodying the present invention reveals the presence of a very thin "skin at the surface of the ingot, casting or shape comprising small copper crystals surrounded by Cu-CuzO eutectic.

The thickness of this skin is generally about 0.008 inch but may vary from less than this value to about 0.04 inch. The oxygen content of this skinaverages about 0.15%. Immediately below the skin, the 'oxygen content drops abruptly to a value which is practically constant throughout the cross section,v although tending to increase slightly adjacent the longitudinal axis of the casting. The average oxygen content of the ingots, castings or shapes of the however, is lower than the average content of vertical wire bars cast from the same metal. For example, oxygen analyses across the crosssection of square wire bars cast in vertical molds and in the present dynamic mold were as follows:

Percentage oxygen content Stationary Dynamic mold mold Skin 0. 103 0. 163 0. 023 0. 022 0. 034 0. 023 Center 0. 031 0. 030 0. 033 0. 022 0. 024 0. 021 Skin 0. 103 0. 163

In conventional vertical cast wire bars, moreover, there was a higher oxygen content near the top than adjacent the bottom. In one bar, for example, the oxygen contents adjacent the bottom, at the center and near the top were 0.033%, 0.040% and 0.045% respectively. The continuous castings of the present invention exhibit no longitudinal segregation and the oxygen content of samples taken at intervals over very long lengths is substantially uniform. For example, one .casting forty seven feet six inches long was tested at intervals along its length, and the oxygen content did not vary more than about 0.001% from the average content of 0.021%. Although the mechanism of the phenomena involved in the present invention has not been fully determined, it is believed that a possible explanation of the formation of the unique structure of the present invention,

growing crystals insures that there can be no cavities nor discontinuities in the crystal structure. By supplying molten metal to the mould in a steady continuous stream, the level of the molten metal in the mould is maintained substantially constant, thus eliminating all possibilities of cold sets, splash marks, or other defects well known to those experienced in the art of casting metals. A further feature of the steady, even supply of metal to the mould is that it permits a stable meniscus to form on the metal at the mould wall, over which the metal continuously feeds as the lower portion of the meniscus is frozen against the mould wall. In this manner a uniform, smooth, continuous skin, substantially free from defects, is formed, the metal readily flowing from the centre of the mould outward to the mould wall, over the meniscus and thereafter becoming the outer surface, or skin, of the casting. The appearance of the structure of the skin may be seen in Fig. 18 which is reproduced from a photomicrograph taken at a magnification of 200 diameters. The specimen was given a light ammonia etch.

Immediately below the skin is located the above mentioned band of chill crystals. The sharpness of the structural transition from the skin to this zone is clearly depicted in Fig. 18, and from this figure, as well as Fig. 19 the general nature of the structure of this zone may :be

, seen. Fig. 19 is reproduced from a photomicrograph taken at a magnification of 100 diameters about below the surface. The grains are equiaxed and vary somewhat in size, becoming larger and merging gradually into the zone of elongated radial crystal aggregates which constitutes the major portion of the casting.

The radial macrograins shown in Fig. 16 are bundles or aggregates-of similarly oriented micrograins, as may be seen in Fig. 20 which was copied from a photomicrograph taken at a magnification of 100 diameters about /2 inch in from an edge of the casting. The crystals or grains shown in Fig. 20 are all within one macrograin.

It will be seen that the micrograins are elongated A and oriented. Like the macrograins, the micrograins of this zone are substantially perpendicular to the adjacent face of the casting. Although the micrograins vary somewhat in size,

. Fig. 20 is typical of the structure throughout the zone of radial crystals.

The vertical crystals of the center zone seen in Figs. 16 and 17 are also columnar aggregates of micrograins, very similar to those of the radial zone except for the different orientation. In the center zone the micrograins are oriented along the longitudinal axis of the casting. In horizontal section the grain boundaries of the micrograms present an angular appearance, as is illustrated in Fig. 21 which was reproduced from a photomicrograph taken at 750 diameters magnification.

From the aforesaid description of the copper ingots, castings or barsEmolded in accordance with the process of the present invention, it will be clear that in cross section they are characterized by metallographic structure comprising four distinct zones, viz., the outer skin, the narrow band of equiaxed chill crystals, the zone of radial crystal aggregates, and the center zone of longitudinal crystal aggregates; that the zone of highest density surrounds the longitudinal axis which, in prior art vertical castings or bars, was the zone of lowest density; and that their composition, structure and properties are substantially uniform and constant throughout their length, whereas prior art vertical or horizontal cast bars varied appreciably in composition, structure and properties from the bottom to the top. Stated in other words, the ingots, castings, shapes or bars of the present invention are characterized by the unique combination of crosssectional symmetry and longitudinal uniformity of composition, structure and properties. This important combination of features is impossible to obtain in ingots, castings or bars cast .in vertical or horizontal molds, and as a consequence new results are achieved in the manufacturing and physical properties of the metal cast in the apparatus and according to the process embodying the present invention. In order to illustrate the advantages and benefits to be obtained in this regard from the present invention, the following specific example is given of manufacturing and physical, tests performed on five tons of tough-pitch copper bars cast as described hereinabove. These bars were 3" square in crosssection with well radiused comers, as illustrated in Fig. 16. They were cut in 54" lengths and the bars were double pointed to facilitate rolling, as those skilled in the art will understand.

A. MANUFACTURING PROPERTIES 1. Hot rolling The bars were hot rolled to both A." and rod, employing a starting temperature of about 800 C. One bar was rolled to hot rolled strip of dimensions 0.232" x 1.125". In all cases the copper behaved satisfactorily, no trouble of any kind being encountered.

2. Open furnace annealing and cleaning Where open furnace annealing was carried out the material behaved in a thoroughly satisfactory manner. Pickling was carried out readily in hot dilute sulphuric acid when performed in the normal manner.

3. Drawing Drafts used in drawing 0.097" wire from 0.250" rod.

4. Cold rolling The above mentioned 0.232" x 1.125" hot rolled strip was annealed in an open furnace, pickled, drawn to 0.145" x 1", and then annealed for about 1 hours in a steam atmosphere in a muflle furnace at about420 C. It was then passed to 2-high cold rolling mills and was rolled in three passes to .0625" with semi circular edges, grooved edging rolls being used in each case. The coil was then annealed in an electric furnace at a temperature of 380 C. for a period of one hour, using an inert atmosphere. The results were exceptionally good, being superior to those obtainable with horizontal or vertical wire bars'oi the prior art. In order to test the strip for edge cracks or defects, test specimens 24" long taken from each end of the coil were bent on edge round a radius of A," through an angle of 180. The bending apparatus was so made that the test pieces were bent without any tension although no side movement was permitted. A lubricant was applied before commencement of the test to ensure evenness of bending. All the specimens successfully withstood the diameter bend without any signs of distress. I As this diameter is about one half the width of the specimen, the result shows absence of cracks and defects and a high capacity for edge bending.

In order further to test the cold rolling properties, one of the coils of 0.097" hard drawn wire referred to hereinabove was divided into seven lengths and cold rolled on a 10" diameter 2-high mill at a speed of approximately 300 feet per minute in a single pass without edge support to the dimensions given in Schedule I.

The edges were carefully examined for side cracking at all stages using a hand glass of low power. No cracks could be detected on any of the samples. The material thus possesses exceptional resistance to edge cracking.

5. Bright annealing During the final annealing process in an inert atmosphere, the copper behaved in a completely acceptable manner and the resulting products were perfectly satisfactory.

B. PHYSICAL PROPERTIES 1. Hard drawn wire tests Test pieces were taken from the ends of each coil of wire drawn from the A" rods of the eleven bars mentioned hereinabove and mechanical tests were applied in accordance with B. S. S. 1'74. The breaking load was determined upon a 2000-lb. Denison hand operated beam testing machine. Twist tests were taken upon a length of 3" using a hand operated twisting machine. Wrapping tests were also taken, the wire being wrapped round its own diameter six times, unwrapped again and again wrapped in the same direction, unwrapping and wrapping until the wire fractured; the figure shown in the table of test results indicates the number of times which the wire was wrapped and unwrapped and the index figure indicates the turn upon which the wire eventually broke. The results of these tests are set forth in Schedule II.

SCHEDULE II Mechanical tests Diam- Breaking Bar No. at" d Twists Wraps .097 HARD DRAWN WIRE Inch Pounds 'Nnmber Number B. S. S. .0969 490 26 3 .097 496 66 6' 5G] 55 4 SCHEDULE III .066" HARD DRAWN WIRE B. S. S .0662 230 35 3 19578). S. S. designates British Standard Specification (No. 174 of The figures for both twists and wraps are excellent. In the case of the .097" wire it is the Wraps which are most exceptional whilst the twists recorded for the .066" wire are unusually high G. ELECTRICAL Counoorrvrrir A sample from each of the coils prepared for the hard drawn wire tests at .097" and .066" was annealed in an inert atmosphere furnace at a temperature of about 330 C. for approximately one hour.

The resistance of a 36.00" test piece, immersed in an oil bath, the temperature of which could be read to an accuracy of 0.1 C., was measured by means of a Tinsley 5-dial bridge, using a .001 ohm resistance as standard. Each test piece was weighed to 5 significant figures and the conductivity was calculated as a percentage of the I. E.

C. standard for annealed copper. The results are tabulated in Schedule IV.

SCHEDULE IV GoNnUo'rIvI'rYREsUL'rs .007" diameter wire .066 diameter wire Oonductiv- Conductiv- Bar No. Bar No. ity

Per cent Per cent 1 100. 9 7 100. 8 101. 0 101. 0

factory for tough-pitch copper. o

It will be apparent to thoseskilled in the in the art that the bars of copper cast according to the process embodying the present invention excellent workingproperties, and that the mechanical and physical properties of the products are at least and in some respects superior to cop per cast according to prior art methods. The

combination in the cast bars of the present invention of structural symmetry in cross-section and of longitudinal uniformity of structure and composition is believed to account, at least in part, for the new results in workability and properties of the copper cast as hereinabove described. The 1 presence, moreover, ofthe zone of somewhat lower density in a narrow band adjacent the outer surface and the zone of highest density in the center ofthe ingots, castings and bars of the presentinr-ve'ntion isa distinct advantage over the con l e lf' omvertical cast bars which are 'lowerin I densityover the whole cross section with the'lowjest-density in the center zone. It iswell recog niz d that in working metal to smaller sizes, for

examplej by forging, rolling and drawing,'the

metal adjacent the outer surface is ordinarily Jworkedto a*greater"extent than that at the f ycenter. "The bars of the present invention, in whichthe zone of so'mewhatlower density coin cides practically with the zone where greatest 1 .working occurs, assure a sound worked product that hasnsatisfactorydensity. p

I Thepres'ent invention is applicable also to the production of hollow ingots, castings andshapes. .A suitable apparatus for carryingoutthis modiflcation of the invention is illustrated in Figs. 22

3 and 28-jin whichfthe mold and associated parts I for suppbrtihgfandvibrating it are constructed in the-same manner. asthe apparatus for-casting solidingots, castings or: shapes whichhas been c described in detail hereinabove in'connection with Figs. 1, 2, 3, and 4. This description need a not be repeated here as the corresponding parts have been given the same reference numerals".

In order to simplify the views, the framework for pporting the parts has been omitted'and'the vibrating mechanism for; only one mold section iss'hown. It will beunderstood, however, that each mold section and each core section are provided with vibrating means similartothat shown .inFigs.22and23. ,j

r The mold and core illustrated in Figs. 22 and "23 form a somewhat annular casting ca-vity'adapted for. casting ingots or shapes that are circular'in cross-section and which have a concentric bore. it will be obvious to those skilled i the m, however, that the inner and outer walls of the tube may be contoured asdesiredand thatythe walls I need'n'ot be of uniform thickness. Such shapes. areto be understood as coming within the scope of the term fannular cavity, or "hollow shapes. The bore of the tubular ingot, casting or shape is formed by aldynamic core. 2I3 comprising sec.

,maybe provided-with ducts for cooling nine, if a desired, and are of suflicient length. to-extend from aposition adjacent the bottom of mold I3 some" distance above the top thereof, as illustrated in Fig. 23. Secured'to the extending portion ofthe core section 2 is the head of a T-shapedcoresupporting member 2|8 which is adaptedto I r 2,284,703 .It' will be seen that the conductivity is satis-.'

111 reciprocate in a bearing 22ll suitably mount d on the framework of division or unit A. Re-

ciprocatory movement is imparted to member 2| I by a rotating eccentricdesignated generally by I 6 reference number 221 through a connecting rod. are of exceptionally finev quality, that they have 22s; The connectingrod is articulated to the head 220 and a wristpin 22!, as shown in Figs. 22 and 23. The ends of the connecting rod 222 hand threads which are "screwed into suitably drilled and tapped openings in cross head 22! i and an eccentric head 222. Locknuts 222 lockthe connecting rod and associated parts in any desired position of adjustment. Eccentric head 222 may have substantially the same structure as eccentric jhead 82, being provided with a shoulder onwhich an outer race 23! of a ball bearing 23! may rest and be securely held by a clampplate aoflt-andjcap screws 231. Clamp plate 220 may ggf'ccentricring 49 maybe secured in the desired position of adjustment by a set screw, or the like. -An inner race 24! of ball bearing 23! is..held by flanged eccentric ring 2'49 and disc 250. Cap screws 250a secure disc 250 firmly to the end of shaft 29. A set screw 252 maybe used to lock the eccentric ring 249 in any desired position of -angularadjustment with reference to eccentric end 25l of shaft 39; The center of eccentric-2i! i is offset 180 with respect to the center Bio of eccentric 5l, but otherwise the relation of parts 2Il"and 249 to the shaft 39 is the same as parts I and 49'. Rotation of shaft 39, therefore, pro- I duces reciprocation of the connecting rods 22 and 229 in'opposite directions, 1. e., 180 out of 1 of the connecting rods 29 and 229 is governed the angu'lar setting of eccentric rings 40 and 243,} respectively. o

a {The operation of the apparatus illustrated in Figs. 22 and 23 is not essentially different from the operation of the apparatus depicted in Figs.

1, 2, 3 and 4. To start the machine, a dummy bar is placed in thebottom of the mold, molten metal is poured into the annular cavity. the cooling fluid is turned into the channels in the mold and core sections, the mold and core sections are vibrated, and, when'the' metal at the bottom has'solidifled, the hollow casting, ingot, .or shape is withdrawn at a speed correlated with the rate of pouring and cooling,all as more fully described hereinabove for the apparatus shown in Figs: 1, 2,3 and 4. It will be clear from the foregoing description of the apparatus that'the distance between a mold section and the adjacent core sectionalternately increases and decreases dueto the 180 displacement of the eccentrics 21'. and 221. The mold sections H are atfethe point'of minimum clearance with respect ftoleaci'r other when the core sections are at their point of maximum clearance and vice'versa. Tire ieiitent and frequency of the transverse movements of the mold and core sections are substantially the same when, tubes or hollow shapes are being cast as recommended above for solid ingots, castings. and shapes, viz., about 2 to V thousandths of an inch movement at frequency offabout l00 to 1500 vibrations per minute. The continuous hollow ingots, casting or shapes are characterized by" structural symmetry in crossare advantageously provided with right and left a 2150' serve -as a top closure for theassembly. The "disc 52,.shown in Fig. 4,1; dispensed with and the eccentric end I! vof shaft 29 is extended vertically -into the eccentric 221, as shown in Fig, 23. ,The

phase with each other. The extent of movement 